LOCTITE® HHD 8000R
Caratteristiche e vantaggi
2-part, non-sag, room temperature-cure methacrylate acrylic adhesive system with fast fixture time and excellent bond strength on multiple substrates.
LOCTITE® HHD 8000R is a green, 2-part, non-sag, room temperature-cure methacrylate acrylic adhesive system. It is designed to have fast fixture time and excellent bond strength on multiple substrates including metals and composites. It has high elongation and excellent cold temperature impact strength whilst forming resilient bonds and maintains its strength over a wide range of temperatures.
Leggi tutto
Documenti e download
Cerchi una TDS o un SDS in un'altra lingua?
Informazioni tecniche
| Base chimica | Metacrilato |
| Caratteristiche principali | Allungamento: Elevato allungamento, Colatura: Non cola, Temperatura: Bassa temperatura |
| Durezza shore, Shore D | 64.0 |
| Numero dei componenti | Bicomponente |
| Rapporto di miscelazione in volume | 10 : 1 |
| Resistenza al taglio, Acciaio (sabbiato) | 14.0 N/mm² |
| Temperatura di stoccaggio | 2.0 - 8.0 °C |
| Temperatura di transizione vetrosa (Tg) | 46.0 °C |
| Tempo di fissaggio | 20.0 - 25.0 min. |
| Tipo di polimerizzazione | Temperatura ambiente Polimerizzazione (Ambiente) |
| Indurente | |
| Colore, Indurente | Blu |
| Viscosità, cone & plate, Indurente @ 25.0 °C Shear Rate 20 s⁻¹ | 17500.0 mPa.s (cP) |
| Prodotto miscelato | |
| Viscosità, cone & plate, Prodotto miscelato @ 25.0 °C Shear Rate 20 s⁻¹ | 25600.0 mPa.s (cP) |
| Resina | |
| Colore, Resina | Giallo |
| Viscosità, cone & plate, Resina @ 25.0 °C Shear Rate 20 s⁻¹ | 47500.0 mPa.s (cP) |
LOCTITE® HHD 8000R
2-part, non-sag, room temperature-cure methacrylate acrylic adhesive system with fast fixture time and excellent bond strength on multiple substrates.