LOCTITE® STYCAST US 1195
Caratteristiche e vantaggi
LOCTITE STYCAST US 1195, Urethane, Potting and Encapsulating
LOCTITE® STYCAST US 1195 is formulated for potting electronics or devices for protection against environmental hazards. This material exhibits high hardness compared to other urethane materials allowing improved durability and impact resistance. It's low Tg allows for better thermal cycle performance to meet low temperature requirements in harsh environments. LOCTITE STYCAST US 1195 passed internal flammability testing at 3 mm thickness.
Leggi tutto
Documenti e download
Cerchi una TDS o un SDS in un'altra lingua?
Informazioni tecniche
| Applicazioni | Incapsulamento |
| Aspetto fisico | Liquido |
| Coefficiente di dilatazione termica (CTE), Above Tg | 128.0 ppm/°C |
| Coefficiente di dilatazione termica (CTE), Below Tg | 58.0 ppm/°C |
| Conducibilità termica | 0.67 W/mK |
| Durezza shore, Shore A | 91.0 |
| Numero dei componenti | Bicomponente |
| Rapporto di miscelazione in peso | 11.5 : 100 |
| Rapporto di miscelazione in volume | 13.45 : 100 |
| Resistività di volume | 9.6x10¹⁴ Ohm cm |
| Schema di polimerizzazione, @ 65.0 °C | 4.0 ora |
| Shelf life | 183.0 giorno |
| Temperatura di stoccaggio | 25.0 °C |
| Temperatura di transizione vetrosa (Tg) | -75.0 °C |
| Tipo di polimerizzazione | Polimerizzazione a caldo |
| Indurente | |
| Colore, Indurente | Nero |
| Densità, Indurente | 1.45 g/cm³ |
| Viscosità, Brookfield - RVF, Indurente @ 25.0 °C Spindle 51, speed 5.0 rpm | 40000.0 mPa.s (cP) |
| Prodotto miscelato | |
| Colore, Prodotto miscelato | Nero |
| Densità, Prodotto miscelato | 1.43 g/cm³ |
| Viscosità, Brookfield - RVF, Prodotto miscelato @ 25.0 °C Spindle 51, speed 5.0 rpm | 19000.0 mPa.s (cP) |
| Resina | |
| Colore, Resina | Marrone scuro |
| Densità, Resina | 1.24 g/cm³ |
| Viscosità, Brookfield - RVF, Resina @ 25.0 °C | 55.0 mPa.s (cP) |
LOCTITE® STYCAST US 1195
LOCTITE STYCAST US 1195, Urethane, Potting and Encapsulating