LOCTITE® ECCOBOND FP4802

Známé jako FP4802 30CC SEMCO 50.4G -40CD

Vlastnosti a výhody

LOCTITE ECCOBOND FP4802 is a high purity, liquid encapsulant designed for use in applications utilizing lead-free solder. This product can withstand solder reflow temperatures up to 260°C after being exposed to JEDEC level 2 (85°C/60% RH, 168hours) preconditioning. It was formulated to meet “Green” non-halide objectives of many technical users and for temperature cycling ranges up to -65 to 150°C. LOCTITE ECCOBOND FP4802 features excellent flow properties allowing the material to penetrate fine pitch wires and deep cavities without entrapping voids. A cavity or potting dam is required for flow control. LOCTITE ECCOBOND FP4802 is suitable for bare chip protection of a variety of advanced packages, such as Ball Grid Arrays (BGA’s), Chip Scale Packages (CSP’s), Plastic Ball Grid Arrays (PBGA’s), and full arrays on Low Temperature cofired Ceramic (LTCC).
LOCTITE® ECCOBOND FP4802 is a high purity, liquid encapsulant designed for use in applications utilizing lead-free solder. This product can withstand solder reflow temperatures up to 260°C after being exposed to JEDEC level 2 (85°C/60% RH, 168hours) preconditioning. It was formulated to meet “Green” non-halide objectives of many technical users and for temperature cycling ranges up to -65 to 150°C. LOCTITE ECCOBOND FP4802 features excellent flow properties allowing the material to penetrate fine pitch wires and deep cavities without entrapping voids. A cavity or potting dam is required for flow control. LOCTITE ECCOBOND FP4802 is suitable for bare chip protection of a variety of advanced packages, such as Ball Grid Arrays (BGA’s), Chip Scale Packages (CSP’s), Plastic Ball Grid Arrays (PBGA’s), and full arrays on Low Temperature cofired Ceramic (LTCC).
Oblasti Použití

Technické informace

Extrahovatelný iontový obsah, Chlorid (CI-) 5.0 ppm
Extrahovatelný iontový obsah, Draslík (K+) 5.0 ppm
Extrahovatelný iontový obsah, Sodík (Na+) 5.0 ppm
Koeficient tepelné roztažnosti (CTE), Above Tg 100.0 ppm/°C
Koeficient tepelné roztažnosti (CTE), Below Tg 20.0 ppm/°C
Teplota skelného přechodu (Tg) 50.0 °C
Teplota skladování -40.0 °C
Viskozita, Brookfield - HBT, @ 25.0 °C Spindle 7, speed 10 rpm 80000.0 mPa.s (cP)