LOCTITE® 609 General Purpose Retaining Compound

Caractéristiques et avantages

This high strength, general purpose, anaerobic-curing retaining compound is designed for bonding cylindrical fitting parts. Mil spec.
To lock bushings and sleeves in housings on shafts, augment press fits, or to bond any close-fitting cylindrical parts, LOCTITE® 609 is a good choice. The green, high strength, anaerobic-curing retaining compound cures in the absence of air between close fitting metal surfaces, providing a high-strength and corrosion-free bond. Typical applications include rotor to shafts in fractional and subfractional horsepower motors.
En savoir plus

Documents et téléchargements

Sécurité Fiche de données et RoHs
LOCTITE® 609, 250 ml Flacon 135513 fr-CA
IDH : 135513
EAN 079340609419

Conditionnement : Flacon

Quantité : 10.0/Emballage

LOCTITE® 609, 1 l Flacon 209763 fr-CA
IDH : 209763
EAN 079340609433

Conditionnement : Flacon

Quantité : 4.0/Emballage

LOCTITE® 609, 0.5 ml Tube 234667 fr-CA
IDH : 234667
EAN 079340609051

Conditionnement : Tube

Quantité : 100.0/Emballage

Aucun document trouvé

Informations techniques

Applications Fixation cylindrique, Pour la fixation étroite de pièces cylindriques
Approbations d'agence / certificats / spécifications ASTM D5363, MIL-R-46082B pour designs existants
Caractéristiques clés Fluorescent, Resistance au cisaillement Résistance élevée au cisaillement, Viscosité Basse viscosité
Couleur Vert
Forme physique Liquide
Gravité spécifique, @ 25.0 °C 1.1
Méthode d’application Manuel, Pistolet d'application, Système d'application
Prise en jeu 0.15 mm
Recommandé pour une utilisation avec Métal
Résistance au cisaillement, Acier 2300.0 psi (15.0 N/mm² )
Temps d'ajustement 10.0 min
Température de service -65.0 - 300.0 °F (-55.0 - 150.0 °C )
Type de polymérisation Polymérisation Anaérobie
Viscosité 120.0 mPa.s (cP)