LOCTITE® 518

Features and Benefits

LOCTITE 518 is a medium-strength, general purpose gasketing product with excellent contamination tolerance. Ideal for use on casted iron, steel and aluminum flanges.
LOCTITE® 518 cures when confined in the absence of air between close-fitting metal surfaces. It is an anaerobic gasketing material designed for use on rigid iron, aluminum, and steel flanged mating surfaces. LOCTITE 518 fills gaps up to 0.25mm and forms a flexible, chemical-resistant seal that will not tear or decay. Parts disassemble easily, even after extended service. Typical applications include sealing close-fitting joints between rigid metal faces and flanges. It is also used as a formed-in-place gasket on rigid flanged connections, e.g. transmissions and motor housings.
  • Semi-flexible, medium-strength anaerobic flange gasket
  • For active and inactive rigid metal flanges
  • Cures through minor surface contamination
  • Adapts to flange surface irregularities and gaps up to 0.25 mm
  • Gel-type consistency
  • Seals instantly against low pressure
  • Reduces inventory costs – no need for large inventory of cut gaskets
  • Resists high pressure when fully cured
  • No compression set or misaligned gaskets
  • Easy to automate
  • Reduces process costs – eliminates manual assembly of conventional gaskets
  • NSF P1 Reg. No. 123758
Read More

Technical Information

Application method Dispense System, Manual
Applications Rigid Assembly Gasketing, Sealing
Chemical basis / base Dimethacrylate Ester
Colour Red
Cure type Anaerobic Cure
Fixture time, Steel 25.0 min.
Gap fill, Unprimed 0.25 mm
Key characteristics Fluorescent, For machined, rigid flanges, Immediate Low Pressure Sealing, Strength: Medium Strength, Surface Contamination-Tolerant, Thixotropic
Number of components 1 Part
Operating temperature -55.0 - 150.0 °C (-65.0 - 300.0 °F )
Physical form Gel
Recommended for use with Aluminium, Metal: Iron - Cast Iron, Metal: Passive Metal, Metal: Steel
Specific gravity, @ 25.0 °C 1.1
Storage temperature 8.0 - 21.0 °C
Viscosity 750000.0 mPa·s (cP)